Fully Drawn Polyester Yarn (FDY)
Polyester FDY is an abbreviation for Fully Drawn Yarn. In some countries, FDY yarns are also referred to as SDY (spin drawn yarn). FDY is manufactured in a way similar to POY, except that the spinning speed is much more higher. Our manufacturing facilities are equipped with Barmag WingsTM FDY lines, which provide the greatest level of quality and speed. FDY is always utilized as a weft or weave material in the manufacture of textiles. Additionally, it can be knitted or woven with any other filament yarn to make a variety of other fabrics. It is mostly utilized in the manufacture of Home Furnishing Fabrics, Fashion Fabrics, Denim, and Terry Towels.
Processing Technology
1. Produced by continuous polymerization processes, which ensures consistent high quality 、excellent dyeing consistency and dyeing uniformity.
2. Equipped with Oerlikon Barmag systems, all the critical properties such as tenacity, elongation, Uster variation and boiling water shrinkage are monitored during the process.
4. High package weight, more efficiency in the subsequent processing processes.
5.Perfect package build for higher downstream speeds and an optimum success rate for automatic yarn transfer, ensuring a high level of production efficiency and low rate of breakages throughout the warping process.
PHYSICAL PROPERTIES | |
Denier % | Avg. 2 |
TenacitycN/dtex | Min. 3.8 |
Elongation % | Avg. 30 |
Uster % | Max. 2 |
Color fastness(Grade) | Above 4.5 GRADE |
Intermingle | Avg. 20 |
Application
Weaving, knitting, braiding, narrow weaving and technical applications
Apparels Fashion Fabrics Sportswear Home Furnishing Fabrics Upholstery Car seat covers
Fully Drawn Polyester Yarn (FDY)
Polyester FDY is an abbreviation for Fully Drawn Yarn. In some countries, FDY yarns are also referred to as SDY (spin drawn yarn). FDY is manufactured in a way similar to POY, except that the spinning speed is much more higher. Our manufacturing facilities are equipped with Barmag WingsTM FDY lines, which provide the greatest level of quality and speed. FDY is always utilized as a weft or weave material in the manufacture of textiles. Additionally, it can be knitted or woven with any other filament yarn to make a variety of other fabrics. It is mostly utilized in the manufacture of Home Furnishing Fabrics, Fashion Fabrics, Denim, and Terry Towels.
Processing Technology
1. Produced by continuous polymerization processes, which ensures consistent high quality 、excellent dyeing consistency and dyeing uniformity.
2. Equipped with Oerlikon Barmag systems, all the critical properties such as tenacity, elongation, Uster variation and boiling water shrinkage are monitored during the process.
4. High package weight, more efficiency in the subsequent processing processes.
5.Perfect package build for higher downstream speeds and an optimum success rate for automatic yarn transfer, ensuring a high level of production efficiency and low rate of breakages throughout the warping process.
PHYSICAL PROPERTIES | |
Denier % | Avg. 2 |
TenacitycN/dtex | Min. 3.8 |
Elongation % | Avg. 30 |
Uster % | Max. 2 |
Color fastness(Grade) | Above 4.5 GRADE |
Intermingle | Avg. 20 |
Application
Weaving, knitting, braiding, narrow weaving and technical applications
Apparels Fashion Fabrics Sportswear Home Furnishing Fabrics Upholstery Car seat covers